Three biodegradable thermoplastic polymers, poly(ε-caprolactone) (PCL), poly(L-lactide-co-D,L-lactide) (PLA) and poly(L-lactide-co-glycolide) (PLGA), have been used to produce nonwovens scaffolds with uniform micrometer fibres. Scaffolds' physical and morphological characterization was performed by X-ray diffraction, Scanning Electron Microscopy and Contact-Angle test. Morphological investigations revealed that all produced fibres were randomly orientated with interconnected pores ranging between 5 and 12 μm in diameter. An average fibre diameter of 1.5, 0.75 and 1.2 μm was found for PCL, PLA and PLGA, respectively. Moreover, experiments were designed to verify whether the fabricated electrospun substrates were biocompatible for ovine amniotic epithelial stem cells (oAECs) under in vitro conditions. Cell adhesion, survival, spatial organization on fibres, proliferation index, and DNA quantification after 48 h culture, showed an enhanced adhesion and proliferation, especially for PLGA scaffolds. The favourable interaction between oAECs and the fibrous scaffolds was attributed to the greatly improved porosity and pore size distribution of the electrospun scaffolds. In addition, AECs can be considered ideal for tissue engineering especially when using biocompatible and opportunely produced scaffolds.
|Titolo:||Amniotic epithelial stem cell biocompatibility for electrospun poly(lactide-co-glycolide), poly(ε-caprolactone), poly(lactic acid) scaffolds|
|Autori interni:||RUSSO, Valentina|
DI MARCANTONIO, LISA
|Data di pubblicazione:||2016|
|Rivista:||MATERIALS SCIENCE AND ENGINEERING. C, BIOMIMETIC MATERIALS, SENSORS AND SYSTEMS|
|Appare nelle tipologie:||1.1 Articolo in rivista|